| 55A
FDA |
| Elastomers |
|
Nominal
Values |
|
Test |
| Tensile
Stress @ 100% |
|
290
psi |
|
ASTM
D412 |
| Tensile
Str @ Break Elast |
|
638
psi |
|
ASTM
D412 |
| Elongation
@ Break Elast |
|
330% |
|
ASTM
D412 |
| Tear
Strength |
|
108
lb/in |
|
ASTM
D624 |
| Tear
Strength Temp |
|
73.4
°F |
|
|
| Compression
Set |
|
23% |
|
ASTM
D395 |
| Compression
Set Temp |
|
73.4
°F |
|
|
| Hardness |
|
Nominal
Values |
|
Test |
| Durometer
Hardness A |
|
55
- |
|
ASTM
D2240 |
| Durometer
Scale |
|
A
Scale - |
|
|
| Durometer
Test Thickness |
|
0.118
in |
|
|
| Thermal |
|
Nominal
Values |
|
Test |
| Brittle
Temperature |
|
-76
°F |
|
ASTM
D746 |
| Electrical |
|
Nominal
Values |
|
Test |
| Arc
Resistance |
|
90
s |
|
ASTM
D495 |
| Flammable |
|
Nominal
Values |
|
Test |
| Flame
Rating - UL, HB |
|
0.0398
in |
|
UL
94 |
| UL
746 |
|
Nominal
Values |
|
Test |
| Rel
Temp Indx Mech w/olmp |
|
203
°F |
|
UL
746 |
| RTI
Mech w/olmp Thick |
|
0.125
in |
|
|
| Rel
Temp Indx Mech w/lmp |
|
158
°F |
|
UL
746 |
| RTI
Mech w/lmp Thick |
|
0.125
in |
|
|
| Rel
Temp Indx Elect |
|
194
°F |
|
UL
746 |
| RTI
Elect Thick |
|
0.0398
in |
|
|
| Comparative
Track Index |
|
600
V |
|
UL
746 |
| High
Volt Arc Track Rate |
|
0.689
in/min |
|
UL
746 |
| Hot
Wire Ignition |
|
45
s |
|
UL
746 |
| Hot
Wire Ignition Thick |
|
0.125
in |
|
|
| High
Ampere Arc Ignition |
|
120
- |
|
UL
746 |
| High
Amp Arc lgn Thick |
|
0.0618
in |
|
|
| |
|