Zinc Plate Mechanical Properties
| Hardness, Brinell |
163 |
163 |
|
| Hardness, Knoop |
184 |
184 |
Converted
from Brinell hardness. |
| Hardness, Rockwell
B |
84 |
84 |
Converted
from Brinell hardness. |
| Hardness, Vickers |
170 |
170 |
Converted
from Brinell hardness. |
| Tensile Strength,
Ultimate |
540 MPa |
78300 psi |
|
| Tensile Strength,
Yield |
415 MPa |
60200 psi |
|
| Elongation at
Break |
10 % |
10 % |
|
| Reduction of Area |
35 % |
35 % |
|
| Modulus of
Elasticity |
200 GPa |
29000 ksi |
Typical
for steel |
| Bulk Modulus |
140 GPa |
20300 ksi |
Typical
for steel. |
| Poisson's Ratio |
0.29 |
0.29 |
Typical
For Steel |
| Machinability |
160 % |
160 % |
Based
on 100% machinability for AISI 1212 steel. |
| Shear Modulus |
80 GPa |
11600 ksi |
Typical
for steel. |
Electrical Properties |
|
|
| Electrical
Resistivity |
1.74e-005 ohm-cm |
1.74e-005 ohm-cm |
Typical
steel |
Thermal Properties |
|
|
| CTE, linear 20°C |
11.5 µm/m-°C |
6.39 µin/in-°F |
Typical
steel |
| CTE, linear 250°C |
12.2 µm/m-°C |
6.78 µin/in-°F |
Typical
for steel ; 0-300°C (68-570°F) |
| CTE, linear 500°C |
13.9 µm/m-°C |
7.72 µin/in-°F |
Typical
for steel ; 0-500°C (68-930°F) |
| CTE, linear 1000°C |
14.7 µm/m-°C |
8.17 µin/in-°F |
Typical
steel |
| Specific Heat
Capacity |
0.472 J/g-°C |
0.113 BTU/lb-°F |
Typical
steel |
| Thermal
Conductivity |
51.9 W/m-K |
360 BTU-in/hr-ft²-°F |
Typical
steel |
| |
|